Ghosh, D. and Mukherjee, S. and Das, S. and Mitra, S.K. (2016) Effect of yttria(Y2O3) coating for high temperature oxidation resistance of 9Cr-1Mo steel. Protection of Metals and Physical Chemistry of Surfaces, 52 (4). pp. 737-743.

Full text not available from this repository.

Abstract

This paper investigates the effect of yttria (Y2O3) coating on high temperature oxidation behaviour of low alloy 9 Cr–1Mo steel. The superficial coating is Y2O3 was prepared for experimental investigation. The isothermal corrosion study of uncoated and coated specimens was carried out in air oxidation environment at 973 K for 8 h. The corrosion rate and reaction kinetics were studied and the post corroded scales were characterized in SEM, EDS and XRD. The results clearly indicate that Y2O3 coated specimen improves the high temperature oxidation resistance than uncoated specimens. The improvement of oxidation resistance in presence of Y2O3 coating can be attributed to the changed mechanism of scale growth from outer cation migration to inner anion migration and enhancement of scale adhesion with the substrate. Further, enhancement of scale adhesion with the substrate in case of Y2O3 coating also improves the oxidation resistance. The detail mechanism of the oxidation of Y2O3 coated and uncoated specimen is further discussed in this paper.

Item Type: Article
Subjects: Materials
Depositing User: Dr. Sarita Ghosh
Date Deposited: 13 Jun 2017 14:06
Last Modified: 13 Jun 2017 14:06
URI: http://cmeri.csircentral.net/id/eprint/361

Actions (login required)

View Item View Item